,Ni and Cu intermetallic compounds.A fusion layer from the bonding interface into Al1100 substrate was observed which was due to the released heat from the combustion synthesis reactions and caused the diffusion of Nickel into the substrate as well as a...

of the intermetallic FeNi phase and particle size of

Al2O3 in the 720 min milled FeNi-30wt.%Al2O3 nanocomposite sample were calculated 28nm and

5.15 μm, respectively. Microhardness results also showed the same sample had the maximum

hardness value...

Hot dip aluminizing (HDA) of low carbon steel in aluminum bath containing various amounts of silicon and manganese was studied in this work. The effect of bath alloying elements on the morphology and growth kinetics of intermetallic layer during...

The magnetostriction and thermal expansion of Er2Fe14−xCoxB (x = 1, 3 and 5) intermetallic compounds were measured, using the strain gauge method in the temperature range 75–450 K under applied magnetic fields up to 1.5 T. For all samples...

attacked sites

observations. It was observed that the Al-rich regions proximate the dispersed Cu particles and Cu–Al

intermetallics were most susceptible to corrosion attack initiation due to a galvanic driving force...