The thermal expansion and magnetostriction of Nd2Fe14Si3 polycrystalline intermetallic compound was

measured, using the strain gauge method in the temperature range 77–590 K under applied magnetic

fields up ...

There are large differences between theoretical and experimental reports on the phase transition points of alkali alanates, which motivated us to study the pressure phase transitions using Density Functional Theory. After ...

Different preparations of complex hydrides lead to different hydrogen uptake and release.

Besides, Potassium Aluminum hydride is a structure with different re/dehydrogenation

properties than the rest of ...

The magnetostriction of the off-stoichiometric R2Fe17-type intermetallic compounds based on R2Fe14−xCoxSi2 (R=Y, Er, Tm and x=0, 4) was measured, using the strain gauge method in the temperature range 77–460 K under applied ...

Magnetoelastic properties of the Pr6Fe11Ga3 alloy are studied by magnetostriction and thermal expansion measurements. The effects of short- and long-range magnetic ordering processes about Curie temperature clearly appear ...

The magnetostriction and thermal expansion of Er2Fe14−xCoxB (x = 1, 3 and 5) intermetallic compounds were measured, using the strain gauge method in the temperature range 75–450 K under applied magnetic fields up to 1.5 ...

The structural and magnetoelastic properties of polycrystalline samples of Y3Fe27.2Cr1.8

and Ce3Fe25Cr4 intermetallic compounds are investigated by means of X-ray diffraction,

thermomagnetic, thermal expansion ...

In this research the magnetoelastic properties of Nd6Fe13 -x Co xCu (x = 0 and 1) intermetallic compoundes are investigated. Analysis of X-ray diffraction patterns indicates that a single phase is formed approximately for ...